PENAMBAHAN KAJIAN LIMBAH PLASTIK PADA CAMPURAN ASPAL PANAS TERHADAP NILAI MARSHALL

Oktafirandy, Figgy (2024) PENAMBAHAN KAJIAN LIMBAH PLASTIK PADA CAMPURAN ASPAL PANAS TERHADAP NILAI MARSHALL. Diploma thesis, Universitas Islam Kalimantan MAB.

[img] Text
Keaslian Skripsi Figgy.pdf

Download (106kB)
[img] Text
Pengesahan Figgy.pdf

Download (122kB)
[img] Text
Abstrak Figgy.pdf

Download (92kB)

Abstract

Aspal merupakan salah satu material yang digunakan sebagai bahan pembuatan jalan raya, material ini memiliki hasil akhir yang baik dan nyaman sebagai perkerasan fleksibel. Untuk mengurangi kebutuhan penggunaan aspal sebagai bahan utama, maka dicari bahan tambahan yang dalam pencampuran sifatnya mampu mengatasi kelemahan yang dimiliki aspal contohnya menggunakan plastik. Dalam penelitian ini menggunakan bahan limbah plastik yaitu jenis PET (Poliyethylene Terephthalate) sebagai bahan tambah campuran aspal panas Laston AC-WC dengan kadar plastik 18%, 21%, 24%, 27%, dan 30%. Metode yang digunakan pada penelitian ini adalah metode experimen di Laboratorium Teknik Sipil Universitas Islam Kalimantan Muhammad Arsyad Al-Banjari Banjarmasin dengan menggunakan 30 benda uji, 3 variasi untuk kadar aspal dan 3 variasi persentase penambahan limbah plastik PET. Tujuan penelitian ini adalah untuk mengetahui pengaruh penambahan limbah plastik PET pada campuran lapis aspal beton AC-WC terhadap nilai Marshall dan mengetahui kadar aspal optimum pada variasi campuran limbah plastik. Hasil dari pengujian Marshall didapatkan nilai stabilitas, flow, VMA, di semua penambahan memenuhi spesifikasi, campuran yang tidak memenuhi spesifikasi yaitu nilai VIM yang melebihi batas maksimum rapat dan nilai VFB dikadar plastik 27% dan 30% tidak sampai batas minimum dan penentuan Kadar Aspal Optimum diambil nilai stabilitas tertinggi dikadar plastik 27% sebesar 1288,15 Kg/mm. Kata Kunci: Aspal, Plastik PET, AC-WC, Marshall Asphalt is one of the materials used as a highway construction material, this material has a good finish and is comfortable as a flexible pavement. To reduce the need to use asphalt as the main ingredient, additional ingredients are sought which in mixing are able to overcome the weaknesses of asphalt, for example using plastic. In this study used plastic waste material, namely PET (Polyethylene Terephthalate) as an added ingredient to the hot asphalt mix Laston AC-WC with a plastic content of 18%, 21%, 24%, 27% and 30%. The method used in this study was an experimental method at the Civil Engineering Laboratory at the Islamic University of Kalimantan Muhammad Arsyad Al-Banjari Banjarmasin using 30 test objects, 3 variations for bitumen content and 3 variations in the percentage of addition of PET plastic waste. The purpose of this study was to determine the effect of adding PET plastic waste to the asphalt mixture AC-WC concrete on the Marshall value and to determine the optimum asphalt content in various plastic waste mixtures. The results from the Marshall test obtained stability, flow, VMA values, in all additions that met specifications, mixtures that did not meet specifications, namely the VIM value that exceeded the maximum density limit and the VFB value at 27% and 30% plastic content not up to the minimum limit and the determination of Optimum Asphalt Content the highest stability value was taken at 27% plastic content of 1288.15 Kg/mm.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Aspal, Plastik PET, AC-WC, Marshall
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Figgy Oktafirandy
Date Deposited: 13 Feb 2024 03:44
Last Modified: 13 Feb 2024 03:46
URI: http://eprints.uniska-bjm.ac.id/id/eprint/19860

Actions (login required)

View Item View Item