PENGARUH PENAMBAHAN FLY ASH TERHADAP KUAT TEKAN PADA BETON GEOPOLIMER

Pramesti, Annisa Anggraeni (2024) PENGARUH PENAMBAHAN FLY ASH TERHADAP KUAT TEKAN PADA BETON GEOPOLIMER. Diploma thesis, Universitas Islam Kalimantan MAB.

[img] Text
pengesahan annisa anggraeni.pdf

Download (153kB)
[img] Text
keaslian annisa anggraeni.pdf

Download (117kB)
[img] Text
Abstrak Annisa.pdf

Download (87kB)

Abstract

ABSTRAK PENGARUH PENAMBAHAN FLY ASH TERHADAP KUAT TEKAN PADA BETON GEOPOLIMER (Oleh Annisa Anggraeni Pramesti; Pembimbing: Fitriani Ridzeki, Ir. Eka Purnamasari; 2023; 57) Beton geopolimer ini adalah beton yang ramah lingkungan karna 100% tidak menggunakan semen dan dapat dikembangkan di masa depan sebagai alternatif pengganti beton konvensional karena dengan menggunakan bahan sintesis anorganik melalui polimerisasi. Tujuannya untuk mengetahui komposisi pada beton geopolimer, mendapatkan nilai kuat tekan, dan mendapatkan variasi maksimal. Dalam penelitian ini dilakukan pengujian bahan dengan metode XRF (X-ray Flourenscece) dengan menggunakan campuran beton 2 variasi persentase fly ash dan alkali aktivator 60% : 40%, dan 70% : 30%. Perbandingan yang dipakai Na2SiO3 dan NaOH sebesar 2 : 1 dengan molaritas 10M dengan menggunakan benda uji kubus 15 x 15 cm, kubus 20 x 20 cm, dan silinder 15 x 30 cm. Pengujian kuat tekan beton dilakukan pada umur 28 hari dengan rencana mutu K-300 Kg/Cm2. Dari hasil penelitian terlihat niali kuat tekan yang maksimal terdapat pada benda uji kubus 15 x 15 Cm variasi 70 : 30% dengan nilai kuat tekan 533.27 Kg/Cm2. Kata Kunci : Geopolimer, Fly Ash, Alkali Aktivator, Kuat Tekan   ABSTRACT THE EFFECT OF FLY ASH ADDITION ON THE COMPRESSIVE STRENGTH OF GEOPOLYMER CONCRETE (By Annisa Anggraeni Pramesti; Supervisor: Fitriani Ridzeki, Ir. Eka Purnamasari; 2023; 57) Geopolymer concrete is environmentally friendly concrete because it does not use 100% cement and can be developed in the future as an alternative to conventional concrete because it uses inorganic synthetic materials through polymerization. The aim is to find out the composition of geopolymer concrete, get the compressive strength value, and get the maximum variation. In this study, material testing was carried out using the XRF (X-ray Fluorescence) method using a concrete mixture of 2 variations in the percentage of fly ash and alkaline activator 60%: 40%, and 70%: 30%. The ratio used for Na2SiO3 and NaOH is 2:1 with a molarity of 10M using 15 x 15 cm cubes, 20 x 20 cm cubes and 15 x 30 cm cylinders. Concrete compressive strength testing was carried out at the age of 28 days with a quality plan of K-300 Kg/Cm2. From the results of the study, it can be seen that the maximum compressive strength is found in the 15 x 15 cm cube test object with a variation of 70: 30% with a compressive strength value of 533.27 Kg/Cm2. Keywords : Geopolymer, Fly Ash, Alkali Activator, Compressive Strengt

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Fly Ash, Alkali Aktivator, Kuat Tekan
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Annisa Anggraeni Pramesti
Date Deposited: 28 Mar 2024 05:07
Last Modified: 28 Mar 2024 05:07
URI: http://eprints.uniska-bjm.ac.id/id/eprint/22214

Actions (login required)

View Item View Item