PEMANFAATAN LIMBAH BOTTOM ASH SEBAGAI CAMPURAN PAVING BLOCK DITINJAU DARI BERAT TOTAL PENYERAPAN AIR DAN KUAT TEKAN

ALPIN, M. (2025) PEMANFAATAN LIMBAH BOTTOM ASH SEBAGAI CAMPURAN PAVING BLOCK DITINJAU DARI BERAT TOTAL PENYERAPAN AIR DAN KUAT TEKAN. Diploma thesis, universitas islam kalimantan MAB.

	Text ABSTRAK DAN DAFTAR PUSTAKA.pdf Download (1MB)
	Text LEMBAR PENGESAHAN.pdf Download (362kB)
	Text LEMBAR PERNYATAAN KEASLIAN.pdf Download (270kB)

Abstract

Material abu bekas pembakaran batu bara atau Bottom Ash saat ini merupakan suatu limbah industri yang memiliki sifat pozzolan dapat dimanfaatkan sebagai bahan pengganti agregat halus atau pasir yang bersifat mengikat karena mengandung silika dan aluminium. Salah satu pemanfaatan Bottom Ash adalah sebagai bahan subtitusi dalam pembuatan Paving Blok. Paving Blok merupakan produk bahan kontruksi yang ramah lingkungan, yang dapat dimanfaatkan oleh masyarakat sebagai perkerasan jalan, trotoar, carport dan Iain lain. Penelitian ini bertujuan untuk mengetahui komposisi campuran, kuat tekan dan Penyerapan Air Paving Blok serta efektifitas pada umur 28 hari. Berdasarkan acuan SNI 03-0619-1996 dengan variasi Bottom Ash 0%, 10%, 20%, 30%, 40%, 50%. Penelitian ini menggunakan metode eksperimental yang dilaksanakan di Laboratorium Struktur Program Studi Teknik Sipil Universitas Islam Kalimantan MAB Banjarmasin. Nilai kuat tekan Paving Blok dengan subtitusi Bottom Ash yang dihasilkan 8,73 Mpa, 20,81 Mpa, 11,20 Mpa, 22,70 Mpa, 15,28 Mpa, 16,30. Hasil penelitian menunjukkan bahwa semakin banyak substitusi Bottom Ash yang digunakan dapat menurunkan berat volume, meningkatkan penyerapan air, , dan meningkatkan kuat tekan Paving Block. Kuat tekan optimum sebesar 22,70 MPa dengan substitusi Bottom Ash sebanyak 30%, memasuki kelas mutu B. Kata Kunci : paving blok, kuat tekan, Penyerapan Air, Bottom Ash ABSTRACT UTILIZATION OF BOTTOM ASH WASTE AS A PAVING BLOCK MIXTURE REVIEWED FROM TOTAL WEIGHT, WATER ABSORPTION AND COMPRESSIVE STRENGTH Coal combustion ash or Bottom Ash is currently an industrial waste that has pozzolanic properties that can be used as a substitute for fine aggregate or sand that is binding because it contains silica and aluminum. One of the uses of Bottom Ash is as a substitute material in the manufacture of Paving Blocks. Paving Blocks are environmentally friendly construction material products, which can be used by the community as road pavements, sidewalks, carports and others. This study aims to determine the composition of the mixture, compressive strength and Water Absorption of Paving Blocks and their effectiveness at the age of 28 days. Based on the reference SNI 03-0619-1996 with variations of Bottom Ash 0%, 10%, 20%, 30%, 40%, 50%. This study uses an experimental method carried out in the Structure Laboratory of the Civil Engineering Study Program, Islamic University of Kalimantan MAB Banjarmasin. The compressive strength values of Paving Blocks with Bottom Ash substitution were 8.73 MPa, 20.81 MPa, 11.20 MPa, 22.70 MPa, 15.28 MPa, and 16.30 MPa. The results showed that increasing the amount of Bottom Ash substitution used could reduce the volume weight, increase water absorption, and increase the compressive strength of the Paving Blocks. The optimum compressive strength was 22.70 MPa with 30% Bottom Ash substitution, entering quality class B. Keywords: Paving Blocks, compressive strength, water absorption, Bottom Ash.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Kata Kunci : paving blok, kuat tekan, Penyerapan Air, Bottom Ash
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Faculty of Engineering, Science and Mathematics > School of Engineering Sciences
Depositing User:	M. Alpin
Date Deposited:	16 Mar 2026 03:34
Last Modified:	16 Mar 2026 03:34
URI:	http://eprints.uniska-bjm.ac.id/id/eprint/33801

Actions (login required)

View Item