PENGARUH PENGGUNAAN BOTTOM ASH SEBAGAI PENGGANTI AGREGAT HALUS PADA CAMPURAN BETON F’c 20 TERHADAP KUAT TEKAN BETON

RIZAL, RIZAL (2021) PENGARUH PENGGUNAAN BOTTOM ASH SEBAGAI PENGGANTI AGREGAT HALUS PADA CAMPURAN BETON F’c 20 TERHADAP KUAT TEKAN BETON. Diploma thesis, universitas islam kalimantan MAB.

[img] Text
ARTIKEL RIJAL_.pdf

Download (190kB)

Abstract

Pembangunan dalam bidang konstruksi kini berjalan dengan pesat. Hal tersebut berhubungan dengan ke ekonomisan bahan material dari kotruksi tersebut. Sehubungan dengan itu perlu diusahakan adanya bahan alternatif yang memiliki sifat-sifat yang serupa dengan material pembuat beton. Salah satu material yang memiliki sifat dan bentuk yang serupa dengan material pembuat beton yaitu abu bottom ash,material ini serupa dengan agregat halus pasir. Tujuan penelitian buat mengetahui karakteristik,kuat tekan beton dan apakah bottom ash bisa dipakai. Pengujian dilakukan di Laboratorium Struktur dan Bahan Politeknik Negeri Banjarmasin. Pengujian terdiri atas pengujian semen,agregat kasar,agregat halus,bottom ash dan beton memakai metode satandar SNI. Dari hasil penelitian karakteristik bottom ash dibisa berat jenis bulk 2,507,berat jenis SSD 2,557,berat jenis semu 2,639,penyerapan 2,010 %,modulus kehalusan 3,71 %,berat isi lepas 1,188,berat isi padat 1,313,zat organik no 3,kadar lumpur 2,4%,kadar air 1,960% memenuhi standar SNI. Berdasrkan dari hasil kuat tekan beton memakai bottom ash sebesar 18,03 MPa dan beton normal 22,42 MPa buat beton memakai bottom ash belum mencapai mutu yang direncanakan 20 MPa,dalam percobaan ini penggunaan bottom ash belum efektif dipakai pada campuran beton. Development in the construction sector is now running rapidly. This relates to the economics of the materials of the construction. In this regard,it is necessary to seek alternative materials that have similar properties to the concrete making materials. One of the materials that has similar properties and shapes to the material for making concrete is bottom ash,this material is similar to fine aggregate of sand. The purpose of the study was to determine the characteristics,compressive strength of concrete and whether bottom ash can be used. The test was carried out at the Structure and Materials Laboratory of the Banjarmasin State Polytechnic. The test consists of testing cement,coarse aggregate,fine aggregate,bottom ash and concrete using the SNI standard method. From the results of the research on the characteristics of bottom ash,the bulk density was 2,507,SSD specific gravity was 2,557,apparent density was 2,639,absorption was 2,010%,fineness modulus was 3.71%,loose density was 1.188,solid density was 1,313,organic matter no. 2.4%,1.960% water content meets SNI standards. Based on the results of the compressive strength of concrete using bottom ash of 18.03 MPa and normal concrete of 22.42 MPa for concrete using bottom ash it has not reached the planned quality of 20 MPa,in this experiment the use of bottom ash has not been effectively used in concrete mixtures.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Beton,Kuat Tekan,Bottom Ash
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Rizal
Date Deposited: 01 Sep 2022 02:22
Last Modified: 01 Sep 2022 02:22
URI: http://eprints.uniska-bjm.ac.id/id/eprint/8621

Actions (login required)

View Item View Item