ANALISA PENGARUH VARIASI ARUS LAS SMAW TERHADAP KEKERASAN DAN KEKUATAN TARIK SAMBUNGAN LAS TAK SEJENIS ANTARA SS400 DENGAN HARDOX400

hidayat, Elwyn rahmat (2021) ANALISA PENGARUH VARIASI ARUS LAS SMAW TERHADAP KEKERASAN DAN KEKUATAN TARIK SAMBUNGAN LAS TAK SEJENIS ANTARA SS400 DENGAN HARDOX400. Diploma thesis, Universitas Islam Kalimantan MAB.

[img] Text
Jurnal ELwyn RH 18620004 ..pdf

Download (207kB)

Abstract

Seiring dengan banyaknya cacat las yang terjadi pada sambungan las tak sejenis antara Hardox400 dengan SS400 pada Vessel Dump Truck, maka diperlukan pengujian material menggunakan benda uji untuk mengetahui variasi sambungan las agar dapat menghasilkan hasil pengelasan yang maksimal. Nilai yang menjadi acuan adalah kekuatan tarik benda uji dan nilai kekerasan pada masing-masing material uji. Dalam penelitian ini, dibuat sambungan las antara Hardox400 dengan SS400 menggunakan pengelasan SMAW dengan variasi arus 80A,100A, dan 120A. Setelah melakukan pengujian didapat nilai kekuatan tarik untuk spesimen 80A adalah 26,41 Kgf/mm², spesimen 100A adalah 27,16 Kgf/mm², dan spesimen 120A adalah 28,20 Kgf/mm². Sedangkan nilai kekerasan rata-rata SS400 setelah dilakukan pengelasan adalah 699HB, 740HB, dan 837HB. Dan untuk Hardox400 adalah 720HB, 780HB, dan 877HB. Dari pengujian sambungan las tak sejenis ini didapat bahwa arus 120A memiliki kekuatan tarik dan kekerasan tertinggi. Along with the many welding defects that occur in dissimilar welding joints between Hardox400 and SS400 on Vessel Dump Trucks, it is necessary to test the material using test specimens to determine variations in welded joints in order to produce maximum welding results. The reference values are the tensile strength of test specimens and the hardness value of each test material. In this study, a welding connection was made between Hardox400 and SS400 using SMAW welding with a current variation of 80A, 100A, and 120A. After testing, the tensile strength values for 80A specimens were 26.41 Kgf / mm², 100A specimens were 27.16 Kgf / mm², and 120A specimens were 28.20 Kgf / mm². While the average hardness value of SS400 after welding is 699HB, 740HB, and 837HB. And for Hardox400 are 720HB, 780HB, and 877HB. From this type of welding connection testing it is found that the current 120A has the highest tensile strength and hardness.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Variasi Arus, Kekuatan Tarik, Nilai Kekerasan Current Variations, Tensile Strength, Hardness Value
Subjects: T Technology > TJ Mechanical engineering and machinery
Depositing User: Elwyn Rahmat Hidayat
Date Deposited: 20 Dec 2021 01:15
Last Modified: 20 Dec 2021 01:15
URI: http://eprints.uniska-bjm.ac.id/id/eprint/8977

Actions (login required)

View Item View Item