PENGARUH PEMANFAATAN LIMBAH LAS KARBIT SEBAGAI PENGURANGAN BAHAN SEMEN TERHADAP KUALITAS KUAT TEKAN MORTAR DENGAN VARIASI PROPORSI YANG BERBEDA

Syahriadi, Syahriadi (2021) PENGARUH PEMANFAATAN LIMBAH LAS KARBIT SEBAGAI PENGURANGAN BAHAN SEMEN TERHADAP KUALITAS KUAT TEKAN MORTAR DENGAN VARIASI PROPORSI YANG BERBEDA. Diploma thesis, Universitas Islam Kalimantan MAB.

[img] Text
Artikel Syahriadi 19640268.pdf

Download (612kB)

Abstract

Mortar adalah adukan yang terdiri dari agregat halus (Pasir), bahan pengikat (Semen Portland, Tanah Liat, Kapur) dan Air. Fungsi mortar merupakan matrik pengikat bagian dari penyusun suatu konstruksi, seiring perkembangan dan permasalahan saat ini harga material cenderung mengalami kenaikan dilakukan terobosan pemanfaatan limbah sebagai salah satu alternatif penambahan bahan material, dengan penelitian tentang pengaruh pemanfaatan limbah las karbit sebagai pengurangan semen bertujuan mengetahui kualitas kuat tekan mortar mengunakan variasi 0%, 10% dan 20%. Pengujian dilakukan di Laboratorium Struktur dan Bahan Politeknik Negeri Banjarmasin Kalimantan Selatan menggunakan metode SNI (Standar Nasional Indonesia) dengan pengujian karakteristik bahan yaitu (Semen, Limbah Las Karbit, dan Pasir), penentuan variasi proporsi campuran, perhitungan mix formula, pengujian faktor air semen, pembuatan benda uji, perawatan benda uji (curing), pengujian kuat tekan, dan analisa data uji kuat tekan. Dari penelitian diketahui kuat tekan mortar dengan campuran Limbah Las Karbit terhadap pengurangan semen ada 3 perbandingan memenuhi persyaratan standar Spesifikasi Umum Tahun 2018 (Revisi 2), yaitu perbandingan 0% (Normal) dengan nilai kuat tekan rata-rata sebesar 9,79 MPa, (10%LLK) sebesar 7,90 MPa dan (20%LLK) sebesar 6,65 MPa yang memenuhi persyaratan kuat tekan minimum sebesar 50 kg/cm2 atau 5 MPa pada umur 28 hari dengan terjadinya penurunan setiap proporsinya. Mortar is a mortar consisting of fine aggregate (sand), binder (Portland Cement, Clay, Lime) and Water. The function of the mortar is a binding matrix part of the constituents of a construction, along with developments and current problems, material prices tend to increase, a breakthrough in the use of waste is made as an alternative to adding materials, with research on the effect of using carbide welding waste as cement reduction aims to determine the compressive strength mortar using variations of 0%, 10% and 20%. The test was carried out at the Structure and Materials Laboratory of the Banjarmasin State Polytechnic, South Kalimantan using the SNI method (Indonesian National Standard) by testing the characteristics of the material (Cement, Carbide Welding Waste, and Sand), determining the variation of mixture proportions, calculating the mix formula, testing the cement water factor, manufacture of test objects, treatment of test objects (curing), compressive strength testing, and analysis of compressive strength tests. From the research, it is known that the compressive strength of mortar with a mixture of Carbide Welding Waste to cement reduction, there are 3 comparisons that meet the requirements of the 2018 General Specifications (Revision 2), namely the ratio of 0% (Normal) with an average compressive strength value of 9.79 MPa, ( 10% LLK) of 7.90 MPa and (20% LLK) of 6.65 MPa which meet the minimum compressive strength requirements of 50 kg/cm2 or 5 MPa at the age of 28 days with a decrease in each proportion.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Mortar, Limbah Las Karbit, Kuat Tekan Mortar, Carbide Welding Waste, Compressive Strength
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Syahriadi
Date Deposited: 25 Oct 2021 02:24
Last Modified: 25 Oct 2021 02:24
URI: http://eprints.uniska-bjm.ac.id/id/eprint/8636