PENGARUH CAMPURAN KAPUR TOHOR DAN MATOS SEBAGAI BAHAN STABILISASI TANAH LEMPUNG DITINJAU DARI NILAI KUAT TEKAN DAN KUAT GESER DI KECAMATAN BATI BATI KABUPATEN TANAH LAUT

Sari, Indah Permata (2022) PENGARUH CAMPURAN KAPUR TOHOR DAN MATOS SEBAGAI BAHAN STABILISASI TANAH LEMPUNG DITINJAU DARI NILAI KUAT TEKAN DAN KUAT GESER DI KECAMATAN BATI BATI KABUPATEN TANAH LAUT. Diploma thesis, Universitas Islam Kalimantan MAB.

[img] Text
Artikel Indah Permata Sari (18640251).pdf

Download (372kB)
[img] Text
Lembar pengesahan.pdf

Download (417kB)
[img] Text
Pernyataan keaslian.pdf

Download (316kB)

Abstract

Tanah lempung sangat keras dalam kondisi kering dan bersifat plastis pada kadar air sedang, namun ketika kadar air tinggi, tanah lempung akan bersifat lengket (kohesif) dan sangat lunak, sehingga menyebabkan perubahan volume yang besar karena pengaruh air dan menyebabkan tanah mengembang dan menyusut dalam jangka waktu yang relatif cepat. Tujuan penelitian ini untuk mengetahui pengaruh penambahan kapur dan matos sebagai stabilisasi tanah lempung dari Kecamatan Bati Bati, Kabupaten Tanah Laut Provinsi Kalimantan Selatan menggunakan kapur 5%, 15%, dan 25% dan matos 1% terhadap nilai uji kuat tekan dan kuat geser tanah tanpa rendaman (unsoaked) dengan waktu 0 hari, 4 hari, 7 hari, 14 hari, 28 hari dan nilai uji kuat tekan dan kuat geser tanah rendaman (soaked) dengan waktu 4 hari, serta persentase kadar campuran yang optimal untuk mendapatkan stabilisasi yang baik. Berdasarkan hasil uji Nilai kuat tekan bebas tertinggi pada campuran kapur 25% + matos 1% dengan waktu pemeraman 28 hari didapat nilai kuat tekan sebesar 1,64 kg/cm² titik1 , 1,595 kg/cm² titik 2. Dan untuk nilai kuat geser tertinggi pada campuran kapur 15% + matos 1% dengan waktu pemeraman 28 hari nilai kohesi sebesar 0,320 titik1, 0,315 titik 2, nilai sudut geser 60,156˚ titik 1, 57,002˚ titik 2, dan nilai kuat geser 0,903 kg/cm² titik 1, 0,839 kg/cm² titik 2. Clay is very hard in dry conditions and plastic at moderate water content, but when the water content is high, clay soil will be sticky and very soft, causing large volume changes due to the influence of air and soil swelling shrink in a relatively short period of time. The purpose of this study was to determine the effect of adding lime and matos as clay stabilization taken from Bati Bati District, Tanah Laut Regency, South Kalimantan Province using lime content of 5%, 15%, 25% and 1% on the compressive strength and strength test values. shear strength of unsoaked soil with 0 days, 4 days, 7 days, 14 days, 28 days and the compressive and shear strength test values for soaked soil (soaked) with a time of 4 days, as well as the optimal percentage of mixture to obtain stable stabilization good. Based on the test results, the highest free compressive strength value in a mixture of lime 25% + 1% matos and a curing time of 28 days obtained a compressive strength value of 1,64 kg/cm² point 1, 1,595 kg/cm² point 2. And for the highest value of shear strength at a mixture of lime 15% + matos 1% with a curing time of 28 days, the cohesion value is 0,320 point 1, 0,315 point 2,the shear angle is 60,156˚ point 1, 57,002˚ point 2, and the shear strength value is 0,903 kg/cm² point 1, 0,839 kg/cm² point 2.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Stabilisasi Tanah, Kapur-Matos, Kuat Tekan, Kuat Geser, Kecamatan Bati Bati.
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Indah Permata Sari
Date Deposited: 17 Nov 2022 02:45
Last Modified: 17 Nov 2022 02:45
URI: http://eprints.uniska-bjm.ac.id/id/eprint/13226

Actions (login required)

View Item View Item