ANALISIS PENGARUH LIMBAH LAS KARBIT TERHADAP KUAT TEKAN BETON DENGAN PRESENTASE 5%, 10% DAN 15 % PADA RENDAMAN AIR GAMBUT

Damayanti, Nor Rosy (2024) ANALISIS PENGARUH LIMBAH LAS KARBIT TERHADAP KUAT TEKAN BETON DENGAN PRESENTASE 5%, 10% DAN 15 % PADA RENDAMAN AIR GAMBUT. Diploma thesis, Universitas Islam Kalimantan MAB.

[img] Text
Keaslian Noor Rosy _20240209_0001.pdf

Download (60kB)
[img] Text
Pengesahan Noor Rosy Damayanti_20240209_0001.pdf

Download (113kB)
[img] Text
Artikel Nor Rosy Damayanti.pdf

Download (78kB)

Abstract

Beton merupakan salah satu bahan kosntruksi yang digunakan untuk bangunan gedung, jembatan, dan jalan. Pada umunya beton terdiri dari semen, air, agregat halus dan agregat kasar, seiring perkembangan dan permasalahan saat ini harga material cenderung mengalami kenaikan maka dilakukan terobosan tentang pengaruh limbah las karbit sebagai pengurangan semen yang bertujuan untuk mengetahui kualitas kuat tekan beton menggunakan variasi 5%, 10%, 15% dan proses curing menggunakan air gambut, karena proses penelitian dilakukan di kota Banjarmasin yang memiliki lahan gambut yang cukup luas. Penelitian dilakukan di Labolatorium Struktur Universitas Islam Kalimantan Muhammad Arsya Al Banjari Banjarmasin Kalimantan Selatan menggunakan metode SNI (Standar Nasional Indonesia) dengan penentuan variasi proporsi campuran, perhitungan mix formula, pembuatan benda uji, perawatan benda uji, pengujian kuat tekan, dan analisa data uji kuat tekan. Dari hasil penelitian ini karakteristik bahan semen dan limbah las karbit memenuhi spesifikasi SNI. Komposisi beton normal menunjukkan kuat tekan 296,30 Kg/cm², komposisi beton dengan variasi 5% limbah las karbit menunjukkan kuat tekan 237,04 Kg/cm², komposisi beton dengan variasi 10% limbah las karbit menunjukkan kuat tekan 211,85 Kg/cm², komposisi beton dengan variasi1 5% limbah las karbit menunjukkan kuat tekan 162,86 Kg/cm², maka kuat tekan optimum dari beton dengan variasi limbah las karbit adalah beton dengan varisi 5% limbah las karbit yakni 237,04 Kg/cm². Concrete is a construction material used for buildings, bridges and roads. In general, concrete consists of cement, water, fine aggregate and coarse aggregate, as current problems and developments in material prices tend to increase, a breakthrough was made regarding the effect of carbide welding waste as a reduction of cement which aims to determine the compressive strength quality of concrete using a 5% variation. 10%, 15% and the curing process uses peat water, because the research process was carried out in the city of Banjarmasin which has quite large peatlands. The research was conducted at the Structural Laboratory of the Islamic University of Kalimantan Muhammad Arsya Al Banjari Banjarmasin, South Kalimantan using the SNI (Indonesian National Standard) method by determining variations in mix proportions, calculating mix formula, making specimens, maintaining test objects, testing compressive strength, and analyzing data on strength tests. press. From the results of this study the characteristics of cement and carbide welding waste meet SNI specifications. Normal concrete composition shows a compressive strength of 296.30 Kg/cm², concrete composition with a variation of 5% carbide welding waste shows a compressive strength of 237.04 Kg/cm², concrete composition with a variation of 10% carbide welding waste shows a compressive strength of 211.85 Kg/cm² , the composition of concrete with a variation of 15% carbide welding waste shows a compressive strength of 162.86 Kg/cm², so the optimum compressive strength of concrete with a variation of carbide welding waste is concrete with a variation of 5% carbide welding waste which is 237.04 Kg/cm².

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Beton, Limbah Las Karbit, Kuat Tekan
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Nor Rosy Damayanti
Date Deposited: 17 Feb 2024 03:35
Last Modified: 17 Feb 2024 03:35
URI: http://eprints.uniska-bjm.ac.id/id/eprint/20029

Actions (login required)

View Item View Item