PENGARUH KUAT TEKAN BETON MENGGUNAKAN ABU AMPAS TEBU SEBAGAI BAHAN TAMBAH PADA BETON K-250

Kurniawan, Denny (2025) PENGARUH KUAT TEKAN BETON MENGGUNAKAN ABU AMPAS TEBU SEBAGAI BAHAN TAMBAH PADA BETON K-250. Diploma thesis, Universitas Islam Kalimantan MAB.

	Text ABSTRAK DENNY KURNIAWAN.pdf Download (180kB)
	Text Lembar pengesahan.pdf Download (962kB)
	Text Keaslian Skripsi.pdf Download (460kB)

Abstract

ABSTRAK PENGARUH KUAT TEKAN BETON MENGGUNAKAN ABU AMPAS TEBU SEBAGAI BAHAN TAMBAH PADA BETON K-250 Disusun Oleh: Denny Kurniawan, Pembimbing I : Eka Purnamasari, ST, MT, Pembimbing II : Dr (C). Ir Fathurrahman, ST., MT.,IPM.,ASEAN Eng Ampas tebu (baggase ash) adalah campuran dari serat yang kuat, yang mempunyai tingkat higroskopis yang tinggi, dihasilkan melalui penggilingan tebu. Ampas tebu sendiri merupakan hasil limbah buangan yang berlimpah dari proses pembuatan gula kurang lebih 30% dari kapasitas giling (Widodo, 2017). Dari pernyataan tersebut kita bisa memanfaatkan limbah ampas tebu sebagai campuran beton karena memiliki tingkat higroskopis yang tinggi.Abu ampas tebu memiliki kandungan yang sama dengan bahan utama pembentuk semen Portland yaitu silika (SiO2) dan Ferrit (Fe2O3) sehingga dapat dijadikan sebagai pozolan yang selain menggantikan sebagian semen juga dapat meningkatkan kekuatan tekan beton (Gemelly Katrina, 2014). Karena memiliki tingkat kandungan silika yang tinggi abu ampas tebu bisa digunakan sebagai pengganti semen Pengujian dilakukan di Laboratorium Universitas Islam Kalimantan MAB Banjarmasin dengan menggunakan metode SNI. Pengujian terdiri atas pengujian abu ampas tebu dan beton. Pengujian abu ampas tebu: berat jenis, kehalusan, Konsistensi dan waktu pengikatan. Pengujian beton: kuat tekan beton. Dari hasil penelitian karakteristik bahan abu ampas tebu memenuhi spesifikasi SNI. Komposisi campuran untuk beton dengan abu ampas tebu 0 % yaitu semen sebesar 18,05 kg, air sebesar 8,30 kg/lt, agregat kasar 1-2 sebesar 46,05 kg, agregat halus 24,80 kg. Komposisi campuran untuk beton dengan abu ampas tebu 3 % yaitu semen sebesar 18,05 kg, air sebesar 8,30 kg/lt, abu ampas tebu sebesar 0,54 kg, agregat kasar 1-2 sebesar 46,05 kg dan agregat halus 24,80 kg Komposisi campuran untuk beton dengan abu ampas tebu 5% yaitu semen sebesar 18,05 kg, air sebesar 8,30 kg/lt, abu ampas tebu sebesar 0,90 kg, agregat kasar 1-2 sebesar 46,05 kg dan agregat halus 24,80 kg. Hasil kuat tekan karakteristik untuk beton dengan abu ampas tebu 0% didapat sebesar 268,186kg/cm2, beton dengan abu ampas tebu 3% didapat sebesar 237,178 kg/cm2 dan beton abu ampas tebu dengan 5% didapat sebesar 254,264kg/cm2. Kata kunci: Kuat Tekan Beton, Abu ampas tebu. ABSTRACT OF THE EFFECT OF COMPRESSIVE STRENGTH OF CONCRETE USING BAGASSE ASH AS AN ADDITIVE IN K-250 CONCRETE Compiled by: Denny Kurniawan, Supervisor I: Eka Purnamasari, ST, MT, Supervisor II: Dr (C). Ir Fathurrahman, ST., MT., IPM.,ASEAN Eng Baggase ash is a mixture of strong fibers, which has a high hygroscopic level, produced through sugarcane milling. Bagasse itself is an abundant waste product from the sugar manufacturing process of approximately 30% of the milling capacity (Widodo, 2017). From this statement, we can use bagasse waste as a concrete mixture because it has a high hygroscopic level. Bagasse ash has the same content as the main materials that form Portland cement, namely silica (SiO2) and Ferrite (Fe2O3) so that it can be used as a pozolan which in addition to replacing part of cement can also increase the compressive strength of concrete (Gemelly Katrina, 2014). Because it has a high level of silica content, bagasse ash can be used as a substitute for cement The testing was carried out at the Laboratory of the Islamic University of Kalimantan MAB Banjarmasin using the SNI method. The testing consists of testing bagasse ash and concrete. Asbestos ash testing: specific gravity, fineness, consistency and binding time. Concrete testing: compressive strength of concrete. From the results of the research, the characteristics of the bagasse ash material meet SNI specifications. The composition of the mixture for concrete with 0% bagasse ash is cement of 18.05 kg, water of 8.30 kg/lt, coarse aggregate 1-2 of 46.05 kg, fine aggregate of 24.80 kg. The composition of the mixture for concrete with 3% bagasse ash is cement of 18.05 kg, water of 8.30 kg/lt, bagasse ash of 0.54 kg, coarse aggregate 1-2 of 46.05 kg and fine aggregate of 24.80 kg Mixed composition for concrete with 5% bagasse ash, namely cement of 18.05 kg, water of 8.30 kg/lt, ash of bagasse of 0.90 kg, coarse aggregate 1-2 is 46.05 kg and fine aggregate is 24.80 kg. The characteristic compressive strength results for concrete with 0% bagasse ash were obtained at 268.186kg/cm2, concrete with 3% bagasse ash obtained at 237.178 kg/cm2 and concrete with bagasse ash with 5% obtained at 254.264kg/cm2. Keywords: Strong Compressive Concrete, Sugarcane Ash

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Kata kunci: Kuat Tekan Beton, Abu ampas tebu. Keywords: Strong Compressive Concrete, Sugarcane Ash
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Depositing User:	Denny Kurniawan
Date Deposited:	03 May 2025 02:51
Last Modified:	03 May 2025 02:51
URI:	http://eprints.uniska-bjm.ac.id/id/eprint/29298